Polyester Impregnating Resins
Polyester Impregnating Resins
Polyester Impregnating Resins
Product
Product
Product
Base
Base
Base
Properties
Properties
Properties
Recommended for wire size (mm dia)
Recommended for wire size (mm dia)
Recommended for wire size (mm dia)
Class Of Wire
Class Of Wire
Class Of Wire
Cut through for 2 min at °C
Cut through for 2 min at °C
Cut through for 2 min at °C
Heat Shock at 180°C/30 min
Heat Shock at 180°C/30 min
Heat Shock at 180°C/30 min
Tandelta Bent Point °C
Tandelta Bent Point °C
Tandelta Bent Point °C
Bawa 216
Polyester
Polyester
Polyester
High cut through and high processing speed
High cut through and high processing speed
High cut through and high processing speed
0.05-1.0
130
280
6d
100-115
Bawa 231
THEIC Modified Polyester
THEIC Modified Polyester
THEIC Modified Polyester
High speed enamelling machines up to 200 VD with excellent heat shock & electrical properties
High speed enamelling machines up to 200 VD with excellent heat shock & electrical properties
High speed enamelling machines up to 200 VD with excellent heat shock & electrical properties
0.05-1.0
130
300
4d
135-155
Bawa 502
Polyester
Polyester
Polyester
High processing speed and reddish golden coloured wire
High processing speed and reddish golden coloured wire
High processing speed and reddish golden coloured wire
0.05-5.0
130
280
6d
100-115
Bawa 301
Modified Polyester
Modified Polyester
Modified Polyester
Enamel for thicker gauges with better heat shock
Enamel for thicker gauges with better heat shock
Enamel for thicker gauges with better heat shock
0.05-5.0
130
280
4d
100-115
Bawa 027
Modified Polyester
Modified Polyester
Modified Polyester
Good flexibility and adherence
Good flexibility and adherence
Good flexibility and adherence
0.2-5.0
130
240
5d
100-115
Bawa 303
Modified Polyester
Modified Polyester
Modified Polyester
Excellent heat shock
Excellent heat shock
Excellent heat shock
0.05-5.0
155
300
2d
145-165
Bawa 275
THEIC Modified Polyester
THEIC Modified Polyester
THEIC Modified Polyester
High processing speed, high cut through and heat shock
High processing speed, high cut through and heat shock
High processing speed, high cut through and heat shock
0.05-5.0
155
320
2d
155-170
Bawa 235
THEIC Modified Polyester
THEIC Modified Polyester
THEIC Modified Polyester
High processing speed, high cut through and heat sock
High processing speed, high cut through and heat sock
High processing speed, high cut through and heat sock
0.05-5.0
155
340
2d
120-130